- Phase Equilibrium Investigations and Thermodynamic Study of the Y2O3-Ta2O5 System
- Zitierfähige Url:
- https://nbn-resolving.org/urn:nbn:de:bsz:105-qucosa2-1030977
- Quellenangabe
- Journal of phase equilibria and diffusion
Erscheinungsjahr: 2024
Jahrgang: 45
Heft: 6
Seiten: 1260-1275
ISSN: 1863-7345 - Erstveröffentlichung
- 2024
- Abstract (EN)
- Two methods were used to investigate the Y2O3-Ta2O5 system: the equilibration method, which covered temperatures from 1573 to 1973 K, and the DTA method, which reached up to 2473 K. Phase identification was carried out using x-ray diffraction and scanning electron microscopy with energy-dispersive x-ray spectroscopy (SEM/EDX). The temperature of the eutectic reaction, L → YTa3O9 (P) + Ta2O5, was determined to be 2019 K, with the corresponding eutectic composition being 78 mol.% Ta2O5. The study presents evidence that contradicts the existence of the eutectic reaction L → YTaO4 (T) + YTa3O9 (P). Instead, it identifies a peritectic reaction L + YTaO4 (T) → YTa3O9 (P), which was observed at a temperature of around 2075 K. Additionally, the heat capacity of the YTa3O9 (P) phase was measured using differential scanning calorimetry (DSC) over the temperature range from 240 to 1300 K. The results of this experimental investigation will lead to the development of a thermodynamic database for the Y2O3-Ta2O5 system.
- Andere Ausgabe
- Phase Equilibrium Investigations and Thermodynamic Study of the Y2O3-Ta2O5 System
DOI: 10.1007/s11669-024-01137-4 - Freie Schlagwörter (DE)
- Yttriumoxid, Phasenumwandlung, Thermodynamik, Kristallstruktur, Röntgenbeugung, Differential scanning calorimetry, Spezifische Wärmekapazität, Phasendiagramm, Intermetallische Verbindungen, Röntgenstrahlung, Kristallographie, Röntgenstrukturanalyse, Rasterelektronenmikroskopie, Strukturanalyse
- Freie Schlagwörter (EN)
- differential thermal analysis (DTA), differential scanning calorimetry (DSC), experimental phase equilibria, heat capacity, Y2O3-Ta2O5 system
- Klassifikation (DDC)
- 620
- Normschlagwörter (GND)
- Yttriumoxid
- Phasenumwandlung
- Thermodynamik
- Kristallstruktur
- Röntgenbeugung
- Differential scanning calorimetry
- Spezifische Wärmekapazität
- Phasendiagramm
- Intermetallische Verbindungen
- Röntgenstrahlung
- Kristallographie
- Röntgenstrukturanalyse
- Rasterelektronenmikroskopie
- Strukturanalyse
- Verlag
- Springer, Boston, Mass.
- Förder- / Projektangaben
- Deutsche Forschungsgemeinschaft (DFG)
Thermodynamische Untersuchungen und Phasengleichgewichte von Hochleistungsmaterialien für zukünftige Wärmedämmschichten im Materialsystem ZrO2-HfO2-Y2O3-Ta2O5
ID: 314579101 - Sonstige beteiligte Institution
- Technische Universität Bergakademie Freiberg, Freiberg
- Version / Begutachtungsstatus
- publizierte Version / Verlagsversion
- URN Qucosa
- urn:nbn:de:bsz:105-qucosa2-1030977
- Veröffentlichungsdatum Qucosa
- 16.03.2026
- Dokumenttyp
- Artikel
- Sprache des Dokumentes
- Englisch
- Lizenz / Rechtehinweis
CC BY 4.0